    Biogas-slurry derived mesoporous carbon for supercapacitor applications

    Thumbnail
    View/Open
    Abstract (114.1Kb)
    Date
    2017-09
    Author
    Enock, Talam
    King’ondu, Cecil
    Pogrebnoi, Alexander
    Jande, Yusufu
    Metadata
    Show full item record
    Abstract
    This study reports on the transformation of biogas slurry into mesoporous carbon for supercapacitor electrodes. Pore structures have been modified by altering activation time, temperature and KOH/carbon mass ratio. The mesoporous carbons are successively developed as evidenced by type IV isotherms obtained in nitrogen sorption studies. BET, micropore and mesopore surface area of 515, 350, and 165 m2 g−1, respectively as well as a narrow pore width distribution of 3–4.5 nm are obtained. X-ray photoelectron results have confirmed the presence of functional groups of oxygen and nitrogen in the samples which facilitates the pseudocapacitance. The electrochemical measurements in 6 M KOH using a three electrode cell with Ag/AgCl as reference electrode and platinum as counter electrode has been performed. The materials activated at 700 °C, 3:1 KOH to carbon mass ratio, and for 120 min exhibit high specific capacitance of 289 F g−1 at a scan rate of 5 mV s−1. Shortening activation time to 30 and 60 min reduces specific capacitance to 163 and 182 F g−1, in that order. Additionally, at 3:1 KOH to carbon mass ratio and 60 min activation time, specific capacitances of 170 and 210 F g−1 at 600 and 800 °C, respectively are obtained. Moreover, specific capacitance increases with increasing the KOH to carbon mass ratio from 148 F g−1 for 1:1–163 F g−1 for 3:1 at 700 °C. Electrochemical impedance spectroscopy studies demonstrate that material has high conductivity. In addition; capacity retention of 96% after 20,000 cycles is shown at scan rate of 30 mV s−1. The study shows that high performance electrodes can be designed from biogas slurry derived porous carbon.
    URI
    https://doi.org/10.1016/j.mtener.2017.06.006
    https://dspace.nm-aist.ac.tz/handle/20.500.12479/698
    Collections
    • Research Articles

    Nelson Mandela-AIST copyright © 2021  DuraSpace
    Theme by 
    Atmire NV
     

     

    Browse

    All PublicationsCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    LoginRegister

    Nelson Mandela-AIST copyright © 2021  DuraSpace
    Theme by 
    Atmire NV